(Summary description)Customized SILICONE STRUCTURAL SEALANT from China manufacturer refers to the adhesive with high strength, can bear large load, aging resistance, fatigue resistance and corrosion resistance, and has stable performance within the expected life. It is suitable for bearing the bonding of strong structural parts. Non structural adhesive has low strength and poor durability. It can only be used for bonding, sealing and fixing of ordinary and temporary properties, and cannot be used for structural adhesive bonding. NEUTRAL SILICONE WETHERPROOF SEALANT from China manufacturer is a structural adhesive with waterproof function. Silicone glue refers to the adhesive based on silicone rubber. According to different functions, it can be divided into structural adhesive, potting adhesive, sealant, thermal conductive adhesive, flame retardant adhesive and so on.

硅烷改性聚氨酯密封膠PH值測試

(Summary description)Customized SILICONE STRUCTURAL SEALANT from China manufacturer refers to the adhesive with high strength, can bear large load, aging resistance, fatigue resistance and corrosion resistance, and has stable performance within the expected life. It is suitable for bearing the bonding of strong structural parts. Non structural adhesive has low strength and poor durability. It can only be used for bonding, sealing and fixing of ordinary and temporary properties, and cannot be used for structural adhesive bonding. NEUTRAL SILICONE WETHERPROOF SEALANT from China manufacturer is a structural adhesive with waterproof function. Silicone glue refers to the adhesive based on silicone rubber. According to different functions, it can be divided into structural adhesive, potting adhesive, sealant, thermal conductive adhesive, flame retardant adhesive and so on.

發布時間 : 2022-12-4 18:53:27
Views:

將Q235和SPCC冷軋鋼板除油十燥備用，在鋼板表面涂上硅烷改性聚氨酯密封膠在室溫下將鋼板分別置于3%NaCI,1(>%硫酸、1ioNaOH溶液中浸泡，比較其耐化學介質滲透性能。耐中性鹽霧腐蝕實驗依據ASTM B117和GB/T1771-207《色漆和清漆耐中性鹽霧性能的測定》進行實驗。將涂有硅烷改性聚氨酯密封膠的干燥試片放人Q-Fog公司生產的CCT 61)1)鹽霧箱中，將之前配好的質量濃度為5g/L的NaCI溶液倒人鹽霧箱的試液槽rty開純水儀、空氣壓縮機和鹽霧箱，設定實驗程序及實驗f1寸間，分別在?4 h, 4H h, 72 h, 16f3 h取樣，取樣停機時IH7不超過30 min。

取出試板并用清潔的溫水沖洗以除去試板表面上的實驗溶液殘留物，而后立即十燥試板、稱重并檢查試板表面的損壞現象，如氣泡、銹蝕、開裂和剝落程度等。

根據GB/T 2423.3-21)6《電-r.電子產品環境試驗第2部分:試驗方法試驗Cab:恒定濕熱方法》進行恒定濕熱實驗，實驗周期為25h，主要檢查涂覆硅烷改性聚氨酯密封膠后金屬樣品的腐蝕情況，并拍照記錄。實驗條件:溫度4℃，濕度3%。

取少量硅烷改性聚氨酯密封膠樣品薄薄地涂抹在濱化鉀晶片上，使用紅外光譜儀分析樣品的成分。

通過兩種方法測試硅烷改性聚氨酯密封膠的pH值。第一種方法:用蘸水的pH試紙快速貼到剛剛擠出的硅烷改性聚氨酯密封膠上，通過顏色比對測試pH值。第二種方法:將長度約3mm的硅烷改性聚氨酯密封膠快速擠到15mL去離子水中，用玻璃棒攪拌2-3 min.使用pH計測量水溶液的pH值。www.qiquanonline.com